| Compositiones chemicae | ||||||||
| Gradus | Ti | Al | V | Fe maximum | C, maximum | N, maximum | H, maximum | O, maximum |
| Ti-6Al-4V ELI | Bal | 5.5~6.5 | 3.5~4.5 | 0.25 | 0.08 | 0.05 | 0.012 | 0.13 |
| Gradus V (Ti-6Al-4V) | Bal | 5.5~6.75 | 3.5~4.5 | 0.3 | 0.08 | 0.05 | 0.015 | 0.2 |
| Proprietates mechanicae | |||||
| Gradus | Conditio | Robur Tensilis (Rm/Mpa) ≥ | Robur Cedendi (Rp0.2/Mpa) ≥ | Elongatio (A%) ≥ | Reductio Areae (Z%) ≥ |
| Ti-6Al-4V ELI | M | DCCCLX | DCCXCV | 10 | 25 |
| Gradus V (Ti-6Al-4V) | M | DCCCLX | DCCLXXX | 10 | / |
Virgae titanii Ti-6Al-4V ELI a XINNUO productae, cuius microstructura intra A3 pertingere potest, et robur tensile plus quam 1100Mpa attingere potest. Virga titanii pro cochleis spinalibus in implantationibus spinalibus adhibetur, cuius qualitas magni momenti est.
1. Compositiones chemicae a spongia titanii adhibita determinantur; XINNUO grana minore gradus O adhibet;
2. Microstructura temporibus liquefactionis determinatur, XINNUO ter liquefiit per furnum ALD Germaniae importatum;
3. Proprietates mechanicae per processus volutationis et recoctionis determinantur, XINNUO omnes gradus productionis moderatur;
4. Vitia interna et fissurae superficiales per inspectionem qualitatis determinantur, XINNUO detectorem vitiorum currentis turbinalis et detectorem vitiorum ultrasonicum ad singulas vectes examinandas utitur;
5. Superficies virgarum titanii XINNUO a detectore superficiei optico ODE, qui detectionem manualem coniungit, inspicitur;
6. Tolerantia virgarum titanicarum XINNUO per mensuram diametri infra-radiorum examinatur.
Hae omnes rationes ad qualitatem finalem virgarum titanii medicinalium ducunt et qualitatem productorum XINNUO confirmant.